Super Duplex S32760

Apr 16, 2020

Stock nou an Super Duplex 32760 ka apwovizyone nan fey, plak, oswa fom Bar, koupe nan kondisyon espesifik ak vini ak Jaa nan Steels metal kalite setifikasyon.
Sa ki annapre yo se pwopriyete yo nan S32760 Super Duplex:
 Ferritic-austenitic nerjaveei asye.
 ekselan rezistans korozyon kont korozyon an jeneral, estres korozyon bravo, korozyon fatig, pitting, crevis ak ewozyon korozyon ak posede tre wo segonde pwopriyete fos.
 bon weldability, pos soude tretman chale pa nesese.
 Max. Tanperati pou peryod tan ki long nan sevis: 280 ° c (536 °F)/(300 ° c/572 °F posib pou peryod kout).
 kondisyon sifas pou gwo rezistans korozyon: pickled oswa machin.
Aplikasyon
Eleman nan lanme, dlo fatra, dlo lanme desalination ak plant chimik ak agresif klori-ki gen medya egzanp. chale echanjeur, pati separate, compressor ak ponp konpozan, turbin lames.
Enfomasyon teknik
Konpozisyon chimik (mwayen)

C	Si	Mn	CR	Mo	Ni	W	Cu	N	PREN
0,020	0,25	0,55	25,20	3,70	7,00	0,65	0,60	0,22	Min. 40

Standa
UNS S32760
Cho fome
Forge
1280 pou 1000 ° c (2336-1832 °F)
Le refwadisman
Tretman chale
Quenching:
1100 ° C (2012 °F)
Dlo, le (epese anba a 2mm)
Estrikti kom etenn:
1100 ° C (2012 °F)
Dlo, le (epese anba a 2mm)
Estrikti kom etenn:
Ferrite + Austenite
Soude
Weldability nan super duplex 32760 se yon bon. Pwosedi yo soude yo sanble ak sa yo aplike pou klas konvansyonel duplex. Soudure consommables pou metod soude diferan ki disponib.
D
Kapasite nan machin nan super duplex 32760 se siperye nan konparab super duplex klas akoz karakteristik optimisé li yo. Plis detay ki disponib sou demann.
Pwopriyete mekanik
Kondisyon: etenn

Pwodwi	Dimansyon Grande mm	0,2% estres prev N/mm2 min.	Rupture fos N/mm2 min.	Elongation A5 min. L Q T	Fos enpak (ISO-V) J min. L Q T
St, SCH	≤ 250	550	750	25 – – –	70 – – –
Bl	≤ 75	– – 251) – –	– – 55 – –

St = Bar, SCH = Forge,
Bl = fey oswa plak
L = Longitudinal, q = Transverse, T = Tanjansyel
1< 3mm="A80mm">
Vale yo pou lot pwodwi ak dimansyon dwe etabli pa ako.
Hight tanperati pwopriyete
Kondisyon: etenn

0,2% sede fos N/mm ² min.	Tanperati
50 ° C (122 °F)	100 ° C (212 °F)	150 ° C (302 °F)	200 ° C (392 °F)	250 ° C (482 °F)	300 ° C (572 °F)
510	480	445	405	400	395

Pwopriyete fizik
Temik conductivité nan................. 20 ° C (68 °F)...... 15,0.................................... W/(m. K)
Chale espesifik nan......... 450............................................................. K
Elektrik resistivity nan................... 20 ° C (68 °F).............. 0,80..... Om mm2/m
Modil nan lastisite nan.................... 20 ° c (68 °F).............. 250 x 103... N/mm2
Pwopriyete mayetik...................................................................... mayetik

20 ° c und... ° c, 10-6 m/(m. K) nan Ekspansyon temik ant 20 ° c (68 °F) ak... ° c (°), 10-6 m/(m. K) nan	Tanperati	10-6 m/(m. K)
°	˚F
100 ° c	212 °F	13,3
200 ° c	392°F	13,6
300 ° c	572°F	14,0
400 ° c	752°F	170

Modil nan lastisite, 103 N/mm2 nan	Tanperati	103 N/mm2
°	˚F
20 ° c	66 °F	205
100 ° c	212 °F	200
200 ° c	392°F	195
300 ° c	572°F	180
400 ° c	752°F	170

Kom aplikasyon espesyal ak etap pwosesis ki pa ekspreseman mansyone nan sa a deskripsyon pwodwi/fey done, kliyan an pral nan chak ka endividyel yo oblije konsilte nou.