AISI 410 BOTLS
AISI 410 BOTLS
AISI 410 BOTLS
ChimikPwopriyete
Klas | C | Mn | Si | P | S | Cr | Ni | ||
410 | min. | - | - | - | - | - | 11.5 | 0.75 |
Pwopriyete mekanik
Tanperaman Tanperati (° C) | Fòs rupture (MPa) | Sede Fòs 0.2% Prèv (MPa) | Elongasyon (% nan 50 mm) | Dite Brinell (HB) | Enpak Charpy V (J) |
Rkwit * | 480 min | 275 min | 16 min | - | - |
204 | 1475 | 1005 | 11 | 400 | 30 |
316 | 1470 | 961 | 18 | 400 | 36 |
427 | 1340 | 920 | 18.5 | 405 | # |
538 | 985 | 730 | 16 | 321 | # |
593 | 870 | 675 | 20 | 255 | 39 |
650 | 300 | 270 | 29.5 | 225 | 80 |
Pwopriyete fizik
Klas | Dansite (kg / m3) | Modil elastik (GPa) | Mwayèn koyefisyan ekspansyon tèmik (μm / m / ° C) | Konduktiviti tèmik (W / mK) | Espesifik Chalè 0-100 ° C (J / kg.K) | Rezistivite elektrik (nΩ.m) | |||
0-100 °C | 0-315 °C | 0-538 °C | nan 100 ° C | nan 500 ° C | |||||
410 | 7800 | 200 | 9.9 | 11 | 11.5 | 24.9 | 28.7 | 460 | 570 |
Konparezon klas spesifikasyon
Klas | UNS Non | Old Britanik yo | Euronorm | Syèd SS | Japonè JIS | ||
BS | En | Non | Non | ||||
410 | S41000 | 410S21 | 56A | 1.4006 | X12Cr13 | 2302 | SUS 410 |